The evaluation of the corrosion behaviour of Hercules™ alloy

Simple item page
dc.contributor.advisorKnutsen, Robert Den_ZA
dc.contributor.authorNkomo, Duduzile Zamavezien_ZA
dc.date.accessioned2018-02-05T12:51:25Z
dc.date.available2018-02-05T12:51:25Z
dc.date.issued2017en_ZA
dc.description.abstractNi contributes about 60% of austenitic stainless steel manufacturing material price. This means that the price of austenitic stainless steel increases with an increase of Ni. Ni price fluctuation has led to major efforts to reduce its content in austenitic steels. Ni has been replaced with readily available, cheap elements such as Mn and N. Hercules™ is a low Ni austenitic stainless steel alloy that was developed at Mintek in the Advanced Materials Division as part of the new development of low Ni austenitic stainless steels. The typical content of Hercules™ comprises of 2 wt.% Ni, 9 wt.% Mn and 2.5 wt.% N When Hercules™ alloy was tested at Mintek for mechanical properties, it was found that it had higher tensile strength than Type 304 in the hot rolled and annealed condition. Therefore, it was concluded that it can be used for structural applications where high strength is required. The target applications for Hercules™ were reinforcement bars and fasteners. There has been work done in order to improve corrosion resistance of Hercules™ in order for it to be used in corrosive environments or for general purposes. A more corrosion resistant Hercules™ alloy with 0.5 wt.% Mo addition was developed. The current project focused on further characterisation of the corrosion resistance of Hercules™ B (with 0.5 wt.% Mo) and Hercules™ A (without Mo addition) against Type 304 and Type 202. Cyclic polarisation technique was used to test the susceptibility of Hercules™ to pitting, crevice and general corrosion in different solutions. Hercules™ B showed better resistance to pitting in 3.56 wt.% NaCl compared to Hercules™ A and Type 304 but, it showed poor resistance in the presence of an artificial crevice. When the concentration of NaCl was reduced to 1 wt.%, Hercules™ B showed better resistance to crevice corrosion compared to Type 304, while Type 202 consistently showed poor corrosion resistance during each test. Immersion tests in 6 wt.% FeCl3.6H2O were consistent with the results that were obtained from the cyclic polarisation technique. The critical pitting temperature (CPT) test was investigated using 6 wt. % FeCl3.6H2O immersion testing. All test alloys started pitting at 25℃, meaning that they all have a CPT value that is less than 25℃. The results obtained from ten-days immersion and cyclic polarisation test in 5 wt.% H2SO4 were also consistent with each other. All test alloys showed good performance in 5 wt.% H2SO4 by achieving a corrosion rate that is less than 0.1 mm/y. It was therefore, concluded that Hercules™ B has an overall corrosion resistance that is comparable to that of Type 304 in 5 wt.% H2SO4 and 1 wt.% NaCl.en_ZA
dc.identifier.apacitationNkomo, D. Z. (2017). <i>The evaluation of the corrosion behaviour of Hercules™ alloy</i>. (Thesis). University of Cape Town ,Faculty of Engineering & the Built Environment ,Centre for Materials Engineering. Retrieved from http://hdl.handle.net/11427/27276en_ZA
dc.identifier.chicagocitationNkomo, Duduzile Zamavezi. <i>"The evaluation of the corrosion behaviour of Hercules™ alloy."</i> Thesis., University of Cape Town ,Faculty of Engineering & the Built Environment ,Centre for Materials Engineering, 2017. http://hdl.handle.net/11427/27276en_ZA
dc.identifier.citationNkomo, D. 2017. The evaluation of the corrosion behaviour of Hercules™ alloy. University of Cape Town.en_ZA
dc.identifier.ris TY - Thesis / Dissertation AU - Nkomo, Duduzile Zamavezi AB - Ni contributes about 60% of austenitic stainless steel manufacturing material price. This means that the price of austenitic stainless steel increases with an increase of Ni. Ni price fluctuation has led to major efforts to reduce its content in austenitic steels. Ni has been replaced with readily available, cheap elements such as Mn and N. Hercules™ is a low Ni austenitic stainless steel alloy that was developed at Mintek in the Advanced Materials Division as part of the new development of low Ni austenitic stainless steels. The typical content of Hercules™ comprises of 2 wt.% Ni, 9 wt.% Mn and 2.5 wt.% N When Hercules™ alloy was tested at Mintek for mechanical properties, it was found that it had higher tensile strength than Type 304 in the hot rolled and annealed condition. Therefore, it was concluded that it can be used for structural applications where high strength is required. The target applications for Hercules™ were reinforcement bars and fasteners. There has been work done in order to improve corrosion resistance of Hercules™ in order for it to be used in corrosive environments or for general purposes. A more corrosion resistant Hercules™ alloy with 0.5 wt.% Mo addition was developed. The current project focused on further characterisation of the corrosion resistance of Hercules™ B (with 0.5 wt.% Mo) and Hercules™ A (without Mo addition) against Type 304 and Type 202. Cyclic polarisation technique was used to test the susceptibility of Hercules™ to pitting, crevice and general corrosion in different solutions. Hercules™ B showed better resistance to pitting in 3.56 wt.% NaCl compared to Hercules™ A and Type 304 but, it showed poor resistance in the presence of an artificial crevice. When the concentration of NaCl was reduced to 1 wt.%, Hercules™ B showed better resistance to crevice corrosion compared to Type 304, while Type 202 consistently showed poor corrosion resistance during each test. Immersion tests in 6 wt.% FeCl3.6H2O were consistent with the results that were obtained from the cyclic polarisation technique. The critical pitting temperature (CPT) test was investigated using 6 wt. % FeCl3.6H2O immersion testing. All test alloys started pitting at 25℃, meaning that they all have a CPT value that is less than 25℃. The results obtained from ten-days immersion and cyclic polarisation test in 5 wt.% H2SO4 were also consistent with each other. All test alloys showed good performance in 5 wt.% H2SO4 by achieving a corrosion rate that is less than 0.1 mm/y. It was therefore, concluded that Hercules™ B has an overall corrosion resistance that is comparable to that of Type 304 in 5 wt.% H2SO4 and 1 wt.% NaCl. DA - 2017 DB - OpenUCT DP - University of Cape Town LK - https://open.uct.ac.za PB - University of Cape Town PY - 2017 T1 - The evaluation of the corrosion behaviour of Hercules™ alloy TI - The evaluation of the corrosion behaviour of Hercules™ alloy UR - http://hdl.handle.net/11427/27276 ER - en_ZA
dc.identifier.urihttp://hdl.handle.net/11427/27276
dc.identifier.vancouvercitationNkomo DZ. The evaluation of the corrosion behaviour of Hercules™ alloy. [Thesis]. University of Cape Town ,Faculty of Engineering & the Built Environment ,Centre for Materials Engineering, 2017 [cited yyyy month dd]. Available from: http://hdl.handle.net/11427/27276en_ZA
dc.language.isoengen_ZA
dc.publisher.departmentCentre for Materials Engineeringen_ZA
dc.publisher.facultyFaculty of Engineering and the Built Environment
dc.publisher.institutionUniversity of Cape Town
dc.subject.otherMaterials Engineeringen_ZA
dc.titleThe evaluation of the corrosion behaviour of Hercules™ alloyen_ZA
dc.typeMaster Thesis
dc.type.qualificationlevelMasters
dc.type.qualificationnameMSc (Eng)en_ZA
uct.type.filetypeText
uct.type.filetypeImage
uct.type.publicationResearchen_ZA
uct.type.resourceThesisen_ZA
Files
Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
thesis_ebe_2017_nkomo_duduzile_zamavezi.pdf
Size:
8.39 MB
Format:
Adobe Portable Document Format
Description:
Download
Collections
Masters