Synthesis, Characterisation and Device Application of Silicon Nanoparticles produced by Mechanical Attrition

Simple item page
dc.contributor.advisorBritton, David Ten_ZA
dc.contributor.advisorHärting, Margiten_ZA
dc.contributor.authorOdo, Ayodeleen_ZA
dc.date.accessioned2014-08-13T20:08:33Z
dc.date.available2014-08-13T20:08:33Z
dc.date.issued2009en_ZA
dc.description.abstractNanostructured silicon is a promising materials for research because it serves as building blocks for nanotechnological applications, such as nano and quantum electronics, sensors and energy applications. However, many of the synthesis methods come with an increased level of sophistication, and thus the unit cost of material produced is high. The study shows that cheap and mass production of silicon nanoparticles can be achieved e ciently with a topdown process of mechanical attrition, particularly using an orbital pulveriser. The inclusion of the powder in a polymeric binder resulted in a new class of nanocomposite whose electrical properties are promising for devise applications using simple printing processes. Scanning and transmission electron microscopy studies reveal that the powders consist of a wide range of size and shape distribution, with large faceted particles with sizes between 1 ô 3 m and relatively small particles of sizes 40ô100nm. The variation of the average particle size with milling time ts well with a rst order exponential decay model which was used to evaluate the limiting particle size as about 120nm. The structural properties of the nanocomposites was investigated using small angle X-ray scattering, while the electrical properties were investigated by conducting I ô V measurements on a metal-nanocomposite-metal structure. Further tests for electronic properties like eld e ect mobilities were achieved by using the nanocomposite as the active layer in an insulated gate eld e ect transistor structure. Electrical characterisation reveals that the carrier injection and transport is determined by two main factors: the concentration of particles constituting the composite, and the level of external bias voltage on the structure. The nanocomposite systems show a clear percolation threshold for charge conduction. Below the percolation threshold, transport is mainly limited by the matrix or insulating binding medium. Direct tunneling and eld emission (FE) are the major transport mechanism for all concentrations at low voltages, while thermally activated processes, such as hopping and thermionic emission are major contributors at low concentrations. At higher concentrations and eld, Poole-Frenkel and Richardson-Schottky conduction mechanisms, resulting from barrier limiting process in the interface, of the metal contact to an interfacial insulator is dominant. Similar pronounced contribution from space charge limited current process resulting from accumulation of charges at the interface, and traps in the bulk, is pronounced at concentrations above the percolation threshold. The transistors function as ambipolar devices, where the dominance of either carrier is deteri mined by the sign and swing direction of the gate potential. The best transistors fabricated have a hole mobility of 2:63 10ô5cm2=V s and electron mobility 7:81 10ô7cm2=V s.en_ZA
dc.identifier.apacitationOdo, A. (2009). <i>Synthesis, Characterisation and Device Application of Silicon Nanoparticles produced by Mechanical Attrition</i>. (Thesis). University of Cape Town ,Faculty of Science ,Department of Physics. Retrieved from http://hdl.handle.net/11427/6544en_ZA
dc.identifier.chicagocitationOdo, Ayodele. <i>"Synthesis, Characterisation and Device Application of Silicon Nanoparticles produced by Mechanical Attrition."</i> Thesis., University of Cape Town ,Faculty of Science ,Department of Physics, 2009. http://hdl.handle.net/11427/6544en_ZA
dc.identifier.citationOdo, A. 2009. Synthesis, Characterisation and Device Application of Silicon Nanoparticles produced by Mechanical Attrition. University of Cape Town.en_ZA
dc.identifier.ris TY - Thesis / Dissertation AU - Odo, Ayodele AB - Nanostructured silicon is a promising materials for research because it serves as building blocks for nanotechnological applications, such as nano and quantum electronics, sensors and energy applications. However, many of the synthesis methods come with an increased level of sophistication, and thus the unit cost of material produced is high. The study shows that cheap and mass production of silicon nanoparticles can be achieved e ciently with a topdown process of mechanical attrition, particularly using an orbital pulveriser. The inclusion of the powder in a polymeric binder resulted in a new class of nanocomposite whose electrical properties are promising for devise applications using simple printing processes. Scanning and transmission electron microscopy studies reveal that the powders consist of a wide range of size and shape distribution, with large faceted particles with sizes between 1 ô 3 m and relatively small particles of sizes 40ô100nm. The variation of the average particle size with milling time ts well with a rst order exponential decay model which was used to evaluate the limiting particle size as about 120nm. The structural properties of the nanocomposites was investigated using small angle X-ray scattering, while the electrical properties were investigated by conducting I ô V measurements on a metal-nanocomposite-metal structure. Further tests for electronic properties like eld e ect mobilities were achieved by using the nanocomposite as the active layer in an insulated gate eld e ect transistor structure. Electrical characterisation reveals that the carrier injection and transport is determined by two main factors: the concentration of particles constituting the composite, and the level of external bias voltage on the structure. The nanocomposite systems show a clear percolation threshold for charge conduction. Below the percolation threshold, transport is mainly limited by the matrix or insulating binding medium. Direct tunneling and eld emission (FE) are the major transport mechanism for all concentrations at low voltages, while thermally activated processes, such as hopping and thermionic emission are major contributors at low concentrations. At higher concentrations and eld, Poole-Frenkel and Richardson-Schottky conduction mechanisms, resulting from barrier limiting process in the interface, of the metal contact to an interfacial insulator is dominant. Similar pronounced contribution from space charge limited current process resulting from accumulation of charges at the interface, and traps in the bulk, is pronounced at concentrations above the percolation threshold. The transistors function as ambipolar devices, where the dominance of either carrier is deteri mined by the sign and swing direction of the gate potential. The best transistors fabricated have a hole mobility of 2:63 10ô5cm2=V s and electron mobility 7:81 10ô7cm2=V s. DA - 2009 DB - OpenUCT DP - University of Cape Town LK - https://open.uct.ac.za PB - University of Cape Town PY - 2009 T1 - Synthesis, Characterisation and Device Application of Silicon Nanoparticles produced by Mechanical Attrition TI - Synthesis, Characterisation and Device Application of Silicon Nanoparticles produced by Mechanical Attrition UR - http://hdl.handle.net/11427/6544 ER - en_ZA
dc.identifier.urihttp://hdl.handle.net/11427/6544
dc.identifier.vancouvercitationOdo A. Synthesis, Characterisation and Device Application of Silicon Nanoparticles produced by Mechanical Attrition. [Thesis]. University of Cape Town ,Faculty of Science ,Department of Physics, 2009 [cited yyyy month dd]. Available from: http://hdl.handle.net/11427/6544en_ZA
dc.language.isoeng
dc.publisher.departmentDepartment of Physicsen_ZA
dc.publisher.facultyFaculty of Scienceen_ZA
dc.publisher.institutionUniversity of Cape Town
dc.subject.otherPhysicsen_ZA
dc.titleSynthesis, Characterisation and Device Application of Silicon Nanoparticles produced by Mechanical Attritionen_ZA
dc.typeDoctoral Thesis
dc.type.qualificationlevelDoctoral
dc.type.qualificationnamePhDen_ZA
uct.type.filetypeText
uct.type.filetypeImage
uct.type.publicationResearchen_ZA
uct.type.resourceThesisen_ZA
Files
Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
thesis_sci_2009_odo_a.pdf
Size:
6.23 MB
Format:
Adobe Portable Document Format
Description:
Download
Collections
PhD / Doctoral